Zirconia

Classic Zirconia Blank with highest bending strength (1400 MPa) for bridges with up to 14 pontics

Cubic, isostatically pressed zirconia with highest translucency for anterior- or posterior restorations with up to 3 units. Bending strength about 600 Mpa

9-layer (5 layers plus 4 transition layers), tanslucent zirconia with high translucency and higher bending strength (about 1100 Mpa) for copings and fully anatomical restorations for up to 14 units. In the production process, 5 layers of pre-coloured zirconia are layered on top of each other, building 4 transition layers in the process. The result is an extremely natural colour transition for vivid, lively restorations.

The new HT zirconia with increased translucency and high bending strength (about 1100 Mpa) for copings and fully anatomical restorations for up to 14 units. Isostatically pressed with a lifetime warranty

Classic zirconia with highest bending strength (1400 MPa) for bridges with up to 14 pontics

The new HT zirconia with increased translucency and high bending strength (about 1100 Mpa) for copings and fully anatomical restorations for up to 14 units. Isostatically pressed with a lifetime warranty

multidimension, 9-layer, high translucent zirconia. the production process, 5 different layers of pre-coloured Tosoh zirconia powders of different bending strength (≥ 600-1100 MPa) are layered on top of each other, building 4 transition layers in the process.

The result is an extremely natural colour transition for vivid, lively restorations for up to 14 units.

Cubic, isostatically pressed zirconia with highest translucency for anterior- or posterior restorations with up to 3 units. Bending strength about 600 Mpa.

9-layer (5 layers plus 4 transition layers) zirconia with highest translucency for anterior- or posterior restorations with up to 3 units. In the production process, 5 layers of pre-coloured zirconia are layered on top of each other, building 4 transition layers in the process. The result is an extremely natural colour transition for vivid, lively restorations. Bending strength about 600 Mpa

9-layer (5 layers plus 4 transition layers), tanslucent zirconia with higher translucency and high bending strength (about 1100 Mpa) for copings and fully anatomical restorations for up to 14 units. In the production process, 5 layers of pre-coloured zirconia are layered on top of each other, building 4 transition layers in the process. The result is an extremely natural colour transition for vivid, lively restorations.