CopraEasyMill NP
€167.00
Tax included
Isostatic, powder-metallurgical manufactured hard Co/Cr blank
Optimum homogeneity due to isostatic high pressure manufacturing process. Minimal bur wear out due to extremely high homogeneity without “hard islands” and casting segregations as with common Co/Cr blanks. Higher milling speed due to better machinability (like titanium) and lower Vickers hardness. Up to 50% shorter process time in your milling system.
The Facts
Optimal homogeneity due to isostatic high pressure manufacturing process
Minimal mill wareout due to extrem high homogeneity without casting segregations
Nickel- and beryllium free, especially configurated for the requirements of the CAD/CAM technology
Unrestrictedly laserable
Higher milling speed due to better grindability and lower Vickers hardness
Up to 50% shorter process time in your milling system
Blanks from 12 mm with Step Unit
CopraEasy Mill NP CoCr-Blank 98 Ø x 8 mm 1
CopraEasy Mill NP CoCr-Blank 98 Ø x 10 mm 1
CopraEasy Mill NP CoCr-Blank 98 Ø x 12 mm 1
CopraEasy Mill NP CoCr-Blank 98 Ø x 13,5 mm 1
CopraEasy Mill NP CoCr-Blank 98 Ø x 15 mm 1
CopraEasy Mill NP CoCr-Blank 98 Ø x 16 mm 1
CopraEasy Mill NP CoCr-Blank 98 Ø x 18 mm 1
CopraEasy Mill NP CoCr-Blank 98 Ø x 20 mm 1
CopraEasy Mill NP CoCr-Blank 98 Ø x 24,5 mm 1
SDK98080
Comments (0)
No customer reviews for the moment.
Isostatic, powder-metallurgical manufactured hard Co/Cr blank
Optimum homogeneity due to isostatic high pressure manufacturing process. Minimal bur wear out due to extremely high homogeneity without “hard islands” and casting segregations as with common Co/Cr blanks. Higher milling speed due to better machinability (like titanium) and lower Vickers hardness. Up to 50% shorter process time in your milling system.